Abstract
Carbon fibers are unique reinforcing agents for lightweight composite materials due to their outstanding mechanical properties and low density. Current technologies are capable of producing carbon fibers with 90-95% of the modulus of perfect graphite (~1025 GPa). However, these same carbon fibers possess less than 10% of the theoretical carbon fiber strength, estimated to be about 100 GPa.[1] Indeed, attempts to increase carbon fiber rigidity results in lower breaking strength. To develop advanced carbon fibers with both very high strength and modulus demands a new manufacturing methodology. Here, we report a method of manufacturing high strength, very high modulus carbon fibers from a very high molecular weight (VHMW) polyacrylonitrile (PAN) precursor without the use of nanomaterial additives such as nucleating or structure-templating agents, as have been used by others.[2,3]