Abstract
The electrochemical properties of YBaCo1.4Cu0.6O5+δ–xCe0.8Sm0.2O1.9
(YBCC–xSDC, x = 20, 30, 40, 50, wt%) have been investigated for the potential
application in intermediate-temperature solid oxide fuel cells (IT-SOFCs). No
chemical reactions between YBCC cathode and SDC electrolyte, and YBCC and
La0.9Sr0.1Ga0.8Mg0.2O3-δ (LSGM) occur. The thermal expansion coefficient (TEC) of
YBCC cathode decreases with SDC addition. The TEC of YBCC–30SDC cathode is
13.60 ×10-6 K-1 from 30 to 850 oC in air and it exhibits the best electrochemical
performance among the YBCC–xSDC cathodes. The polarization resistance (Rp) of YBCC–30SDC is 0.027 Ω cm2 at 850 oC, 0.044 Ω cm2 at 800 oC and 0.075 Ω cm2 at
750 oC. The maximum power density value of electrolyte-based cell with
YBCC–30SDC cathode is 662, 483 and 319 mW cm−2 at 850, 800 and 750 oC,
respectively. Preliminary results indicate that YBCC–30SDC is especially promising
as a cathode for IT-SOFCs.