Mixed polyanion glass cathodes: Effect of polyanion content

Abstract

Mixed polyanion glass cathodes in lithium-ion batteries have very high capacities (200-500 mAh/g), but currently these materials have fundamental problems with 1st-cycle irreversible loss, cycling efficiency, and capacity fade. It is well established that polyanion substitutions into glasses can dramatically affect their physical properties, but the effect of polyanion content on the electrochemical performance has not been previously established. The proper amount of lithium and borate substitution in copper phosphate/vanadate glasses was shown to nearly eliminate 1st-cycle irreversible loss and improve cycling efficiency. Raman and IR spectroscopy were used to identify polyanions that correlated with electrochemical performance changes.