Mechanical properties and strengthening mechanisms of cold sprayed Al-Mg alloys

Abstract

This paper investigates the mechanical properties and strengthening mechanisms of cold sprayed Al-Mg alloys as a function of Mg content. Cold spray (CS) is a solid-state deposition process that can be used as a repair technique for structural components. However, the limited ductility of cold sprayed materials is an unsettled issue in CS community. Herein, reproducible, and significantly increased elongation to failure (∼15%) in as-deposited conditions is reported in CS Al-Mg binary alloys with low Mg content (≤ 2.5 wt%). Furthermore, reducing Mg content down to 2.5 wt% in CS Al-Mg binary alloys demonstrated comparable mechanical strength to its wrought counterparts. Strengthening mechanisms were analyzed in wrought and CS Al-Mg alloys based upon microstructural characteristics, such as grain size, Mg solute concentration, and dislocation density. A quantitative evaluation of yield strength revealed that grain boundary strengthening is predominant in CS Al-Mg alloys as compared with their wrought counterparts. When comparing among CS Al-Mg binary alloys of different compositions, Mg solute concentration, and dislocation density governed mechanical strength. The underlying mechanism for the variation of mechanical properties and strengthening mechanisms is discussed in terms of these microstructural characteristics.