A modified scheil approach for nucleation-dependent solidification pathways

Abstract

As-solidified microstructures of near-eutectic alloys often contain multiple primary phases that are not expected from equilibrium phase diagrams. Such microstructures are caused by cooling-rate-dependent solidification pathways, a factor not captured by the Scheil–Gulliver model or variations thereof. Here, we present a model and algorithm that incorporate the critical nucleation undercooling for each solid phase into the Scheil–Gulliver model. We hypothesize that the non-equilibrium microstructure formation is primarily governed by a nucleation-competition mechanism. This mechanism accounts for both stable/metastable phase selection and primary-phase formation within eutectic regions driven by asymmetric nucleation barriers. The model is validated against a hypereutectic Al-Fe alloy, where it successfully reproduces the observed microstructural constituents, revealing the key dependencies of solidification microstructure on nucleation kinetics. Applicability to multicomponent systems is demonstrated through a hypereutectic Al–Fe–Si ternary alloy, where the model successfully predicts divorced eutectic microstructures and the associated oscillatory solidification pathways along univariant lines. The proposed framework establishes a nucleation-dependent computational approach for interpreting and predicting solidification microstructures.