Abstract
Ferritic-Martensitic steel welds typically require post weld heat treatment (PWHT) to restore toughness and high temperature performance. This off-line thermal process reduces disparities between weld and base metal, but can cause distortion, cracking, or simply be impractical due to assembly size and joint non-uniformity. Here we show integrated welding and thermal processing applied to modified 9Cr-1Mo (Grade 91) steel, favored for advanced power generation applications, performed in real time through the addition of a secondary heat source near the primary weld head. Optimal integrated processing reduces weld fusion and heat affected zone hardness by 125 HV, approaching performance of conventional 730 °C, 60 min PWHT processing. Microstructures and mechanical performance are compared for mechanized GTAW welds, with equivalent lifetimes noted in cross-weld creep rupture tests up to 234 MPa at 550 °C, and up to 104 MPa at 650 °C. The integrated process was validated on a Grade 91 pressure vessel with multipass cold wire feed GTAW. After 550 °C, 71.4 bar thermomechanical cyclic testing, the maximum weld hardness is <350 HV.