Abstract
Inconel 718 fabricated using laser powder-bed fusion, contains precipitates in the as-built condition that can be coarsened by high-temperature heat treatments. In this study, two homogenization heat treatment regimens were applied to discern the impact of heat treatment conditions on the growth of complex M(C, N) carbonitrides. In the first heat treatment, the samples underwent heat treatment between 1050 °C and 1200 °C for 0.5 h. In the second heat treatment, the samples were held at a constant temperature of 1150 °C, with varied holding times from 0.5 h to 8 h. Heat treatments dissolved the unstable Laves phase, but the carbonitrides persisted in the structure regardless of temperature and duration. Changes in the compositions, lattice parameters, and sizes of M(C, N) carbonitrides were measured using transmission electron microscopy and high-energy synchrotron X-ray diffraction. The results show an Nb enrichment at carbonitrides while Nb loss at the matrix with increased homogenization temperature. The findings suggest the optimum heat treatment conditions to achieve a homogeneous structure and controlled carbonitride size are between 1000 and 1050 °C for up to 2 h.